Svařování jemnozrnných ocelí v autojeřábové technice

Ing. Jaroslav BRABEC

Disertační práce

High strength steel, ?t8/5, heat input, mechanical properties, square groove welding, RapidWeld, S1100QL

Anotace:

Tato disertačni prace se zabyva ověenim vhodnosti využiti metody hlubokych průvarů pro bezukosove svařovani vysokopevnostnich oceli. Cilem hodnoceni vhodnosti metody bylo analyzovat rozdil dosaženych materialovych vlastnosti svaroveho spoje při svařovani za stejnych podminek a popsat procesy, ktere se v důsledku vytvařeni svaroveho spoje iniciuji. Jako zakladni material byla použita vysokopevnostni jemnozrnna ocel S1100QL. V prvni teoreticke časti je popsana vyroba vysokopevne oceli, jsou popsany struktury vysokopevnych oceli, zkoumana metoda svařovani RapidWeld, problematika vneseneho tepla, definice svaroveho spoje použiteho pro experiment a metody pro hodnoceni materialovych vlastnosti spoje. Dale jsou zkoumany okrajove podminky při překročeni doby ochlazovani pod 6 s a přes 12 s, zkoumanim mikrostruktury svaroveho kovu, tepeln. ovlivněne oblasti a zakladniho materialu. V dalši časti prace jsou publikovany dosažene vysledky experimentů, na ktere navazuje zavěr experimentu společně s diskusi. Provedeny experiment prokazal vhodnost metody pro zajištěni požadovanych materialovych vlastnosti u vysokopevnostni jemnozrnne oceli při dodrženi požadovanych parametrů, předevšim vyzkum potvrdil požadavek na dodržovani doby ochlazovani t8/5.

Abstract:

This doctoral thesis assesses the suitability of square-welding high strength steel using the deep penetration welding method, RapidWeld. The aim of the evaluation of the suitability of the method was to analyze the difference in the material properties of the weld joint when welding under the same conditions and to describe the processes that are initiated as a result of the formation of the weld joint. High strength, ultra-fine-grain steel S1100QL (XABO 1100) was used as a parent metal. In the first theoretical part, the production of high-strength steel is described, the structures of high-strength steels are described, the RapidWeld welding method investigated, the issue of heat input, the definition of the weld joint used for the experiment and methods for evaluating the material properties of the joint are described. Further, the boundary conditions are investigated when the cooling temperature is exceeded below 6 s and over 12 s, by examining the microstructure of the weld metal, the heat affected area and the base material. In the next part of the work, the achieved results of the experiments are published, followed by the conclusion of the experiment together with a discussion. The performed experiment demonstrated the suitability of the method for ensuring the required material properties of high-strength fine-grained steel while observing the required parameters; especially the research confirmed the requirement to observe the cooling temperature Ät8/5.

Klíčová slova

vysokopevnostni ocel, ?˘t8/5, vnesene teplo, mechanicke vlastnosti, bezukosove sva.ovani, RapidWeld, S1100QL

Jazyk práce: čeština

Datum vytvoření / odevzdání či podání práce: 9. 5. 2023

Zveřejnit od: 31. 12. 2999

Obhajoba závěrečné práce

• Vedoucí: prof. Dr. Ing. Libor Beneš, IWE

UNIVERZITA JANA EVANGELISTY PURKYNĚ V ÚSTÍ NAD LABEM

Fakulta strojního inženýrství

Doktorský studijní program / obor:
Strojírenská technologie / Strojírenská technologie